Dowlex 2344-E
| Pipe propertis ISO 1186 |
| Temparature [C] |
Hydrostatic stress [MPa] |
Time [h] |
| 20 |
11 |
>10 |
| 80 |
4,6 |
>165 |
| 80 |
4,0 |
>30 000 |
| 95 |
3,7 |
>165 |
| 95 |
3,5 |
>1000 |
| 95 |
3,0 |
>10 000 |
| 110 |
2,1 |
>1000 |
| 110 |
1,9 |
>10 000 |
| Material propertis of Dowlex 2344-E |
| Physical propertis |
Test method |
Value |
| Melt index (190C/2,16kg) |
ISO 1133-4 |
0,7g/10min |
| Melt index (190C/2,16kg) |
ISO 1135-5 |
2,2g/10min |
| Density base resign |
ISO 1183 |
0,933g/cm3 |
| Tensile yield(50mm/min) |
ISO 527 |
16,5MPa |
| Yield elongation(50mm/min) |
ISO 527 |
14% |
| Ultimate tensile(50mm/min) |
ISO 527 |
26MPa |
| Ultimate elongation(50mm/min) |
ISO 527 |
>1000% |
| Flexural Modulus |
ISO 178 |
540Mpa |
| Hardnes |
ISO 868 |
55Shore D |
| Izod impact (23C) |
ISO 180 |
n.b. |
| Izod impact (-40C) |
ISO 180 |
70J/m |
| Vicat softening point |
ISO 306 |
119 C |
|
|
|
|